Protection of welded joints against corrosion degradation
To chci
Welded joints form an integral part of steel constructions. Welded joints are undetachable joints, which are however subjects of corrosion processes. The internal energy increases during the fusion welding especially in the heat affected places around the welded joint, which become initiating spot of corrosion degradation. The aim of the experiment is to put
a welded joint produced by the MAG method to a test of corrosion degradation under the conditions of the norm ČSN ISO 9227 (salt-spray test). Organic and inorganic anticorrosion protections were applied on welded beads. First of all, there were prepared welded beads using the method MAG; secondly, metallographical analyses of welded metal, heat affected places and base material were processed. Further, microhardness as well as analysis of chemical composition using the EDS microscope were analysed. Based on a current trend in anticorrosion protections, there were chosen three types of protective coatings. First protective system was a double-layer synthetic system, where the base layer is formed by paint Pragroprimer S2000 and the upper layer by finishing paint Industrol S 2013. Second protective system is a duplex system formed by a combination of a base zinc coating with Zinorex paint. The last protective system was formed by zinc dipping only. Corrosion resistance of the individual tested samples was evaluated based on degradation of protective coating. The corrosion origin as well as the corrosion process were observed, the main criteria was the observation of welded bead.
… celý popis
Uloženo v:
Podrobná bibliografie
-
Hlavní autor
-
Jiří Votava, 1979-
-
Typ dokumentu
- Články
-
Fyzický popis
- 20 il.
-
Publikováno v
- Acta Universitatis Agriculturae et Silviculturae Mendelianae Brunensis. -- ISSN 1211-8516. -- Roč. 61, č. 6 (2013), s. 1897-1904
-
Témata
-
Popis jednotky
- 17 obr., 1 graf, 2 tabulky
-
Bibliografie
- Literatura na s. 1903-1904